टंगस्टन मशीनिंग

Tungsten can be very difficult to fabricate because of its high hardness and low ductility. Tungsten is a strong, मुश्किल, आम तौर पर कमरे के तापमान पर भंगुर है दरार के प्रति संवेदनशील धातु. It requires special handling and skill beyond that necessary for most metals and alloys. It is important to remember when working with Tungsten is that it must be cut or formed at temperatures well above its transition temperature. Failure to do this may result in cracking or lamination. Care should be taken to insure that the metal remains at this temperature throughout the entire forming process. The use of cold tooling which rapidly chills the metal can be as harmful as not preheating the material. The best method for machining that involves metal removal is E.D.M. The following conventional methods can also be used with great care: पीस, गठन, में शामिल होने, मिलिंग, riveting, कताई, मुद्रांकन, और निर्णायक.

की ओर मुड़ते
उपकरणCarbide H(2)
Clearance angle
वापस रेक27°
ओर रेक
काटने की गति132 ft per minute
Nose Angle90°
नाक त्रिज्या
पीस (Use aluminum oxide or silicon carbide wheels with medium hardness.)
Wheel Typesilicon carbide; hardness j to l ; gram size 100-120
Speed12 ft per second
मिलिंग (When milling Tungsten, the following is recommended)
Cutting speed73 फुट प्रति मिनट
clearance angle
side rake10°
गठन (When spinning, bending or stamping note the following)
टूलींगCarbide
Temperature1000° – 1500° F