超级 – Invar®

Invar® (36% 倪平衡铁) 多年一直低膨胀应用程序选择的金属合金. “Super-Invar®” (31% 镍-5%共同平衡铁) 找到了一些支持,因为它已经近乎于零的有限的温度范围内的热膨胀系数. 有用的范围 “超级 Invar®” 仅限于对-32 ° 之间。 + 275° C. 因为材料开始从奥氏体转变到部位,在温度低于 32 ° F

物理性能:
密度:.0294 lb/cubic inch
硬度:77 RB
Tensile Strength:69,800 防扩散安全倡议
屈服强度:43,900 防扩散安全倡议
Elongation 2″:38%
Modulus of Elasticity:21.5 x 10-6psi
Polasons Ratio:.234
To develop the lowest coefficient of thermal expansion the following heat treatment is recommended:
1525° F 10 min @temperature:water quench or rapid air cool
600° F 60 min @ temperature:air cool
212° F 24 hours@ temperature:air cool
Thermal Expansion:
Temp deg F:Coeff of Expansion:
0°F-50°F02. x 10(-6) in/IN/deg f
50°F-100°F05. x 10(-6) in/IN/deg f
100°F-150°F01. x 10(-6) in/IN/deg f
150°F-200°F07. x 10(-6) in/IN/deg f
Chemistry: (Typical Analysis)
C.05
S.01
Si.09
Mn.39
Ni31.26
Cr.03
.08
Ai.07
Co5.36
Typical Linear Coefficient of Thermal Expansion: ( cm per cm. c x 10 -6 )
30 自 1009.4
30 自 2009.4
30 自 3008.8
30 自 3509.0
30 自 4008.7
30 自 4258.9
30 自 4509.0
30 自 5009.4
30 自 55010.2
30 自 60010.4
30 自 70011.3
30 自 80012.1
30 自 90013.0
30 自 100013.9
合金 52 (Nominal Data Sheet)
镍 (Ni)50.5
Chromium (Cr)0.10
Manganese (Mn)0.60
硅 (Si)0.30
碳 (C)0.05
铝 (Al)0.10
Magnesium (Mg)0.50
锆 (Zr)0.00
Titanium (Ti)0.00
Phosphorus (P)0.025
Sulfur (S)0.025
平衡
Typical Linear Coefficient of Thermal Expansion ( cm per cm. c x 10 -6 )
30 自 10010.5
30 自 20010.4
30 自 30010.2
30 自 35010.2
30 自 40010.1
30 自 425NA
30 自 45010.1
30 自 50010.0
30 自 55010.5
30 自 60010.8
30 自 70011.7
30 自 80012.5
30 自 90013.3
30 自 100014.2

C.T.E 经常跨越零, 每个多热量的行为略有不同, 但这些结果是典型的 0 ° F 和 200 ° F 之间的材料

可成形性: Super Invar® 是很容易形成, 深绘制和制作.

焊接性: 超因瓦合金焊接使用特殊的超因瓦合金焊丝, 和各种其他高镍杆和电线

可加工性: Super Invar® 是艰难和小熊, 不硬或磨料. 工具倾向于犁而不是切, 导致在细长 “芯片。” 工具必须锋利, 进给和速度低,以避免热和失真. 所有加工操作建议使用冷却液. 类似于 Kovar® 的可加工性, 不锈钢 300 系列, 和蒙乃尔合金报. 镍-铁合金一般有一种倾向,在渗透表面的热工作期间发展表面的规模. 为此加工余量必须增加消除深表面氧化. 中的初始切频繁最难的.